Epoxy Resin L + Hardener L (40 minutes) 140g.

Epoxy Resin L + Hardener L (40 minutes), set of two components (140g)

- Free from nonylphenol and DETA
- Low viscosity, solvent- and filler-free
- Fast impregnation of glass, aramid and carbon fibres
- High static and dynamic strength
- Low surface tension, good adhesion and low curing shrinkage
- Ideal for bonding wood, metal, Styropor® etc.

Epoxy resin L with the corresponding hardeners is the most frequently used laminating and bonding resin from the R&G product range.

Epoxy resin L with Hardener L has similar mechanical properties to the laminating systems commonly used in aircraft construction.

Processing time: 40 minutes (100 g / 20 °C)

Mixing ratio:
100 : 40 parts by weight Epoxy Resin L : Hardener L
100 : 45 parts by volume Epoxy Resin L : Hardener L

Curing time (at 23 °C): 24 hours, warm curing optional
Heat distortion temperature: Approx. 70 °C, up to a maximum of 80 °C with an additional 15 hours at 60 °C

Processing:
It can be processed in all common processes such as hand lamination, pressure and vacuum impregnation as well as pressing and winding.

- Material characteristics (pure resin cured) Epoxy Resin L with Hardener L:
- Flexural strength DIN EN ISO 178 in MPa 111
- Bending E-modulus DIN EN ISO 178 in MPa 2950
- Tensile strength DIN EN ISO 527 in MPa 69
- Compressive strength DIN EN ISO 14126 in MPa 91
- Hardness Shore D 90
- Elongation at break DIN EN ISO 178 in % 5.9

CYTOX expert opinion on the Resin System Epoxy Resin L + Hardener L (see below under additional information): this system is not cytotoxic (cell-damaging), important for applications in medical technology