Carbon fabric 160 g/m² style 442-aero,

Carbon fabric 160 g/m² style 442-5 aero, twill weave, non-shift 100 cm R&G

Artikel-Nr.: 190225-SV-100-1
EAN: 4044199104749

USA: width 39.37", weight 4.7 oz/yd²

Fibre: Tenax® HTA 40 / 200 tex (3k)

Style 442-5 aero, non-shift

Material as per aviation standards

Setting (Thr./cm): 4 x 4
Twill weave
Width: 100 cm

Basic weight 160 g/m² + 10-15 g/m² EP binder

Application:
Standard reinforcement fabric for modelling, motorsports, marine construction, and sporting equipment.

The fabric is coated on one side with an EP-Binder, backside is smooth.

The EP binder prevents slippage, so cut pieces do not loose threads. Heat (pressure mould) can be used to preform the fabric before impregnation with resin. Specifically for carbon designs in automotive engineering. Even an iron on the surface (eg during coating of surfaces) is possible. The fabric will be formed only and has additionally to be impregnated with resin.

If the fabric is processed during normal hand laminating without melting the binder, please make sure that the smooth side is placed on the later visible side of the mould. Otherwise too many small air bubbles will form because the fabric does not lie flat due to the "droplets" of the EP binder.

Calculated data for hand laminates with 35 volume per cent fibres:
Resin consumption: 193 g/m², laminate thickness: 0.26 mm, laminate weight: 353 g/m²

Scopy of delivery:
- 1m Carbon fabric 160 g/m²